Light burnt magnesium ball light burnt magnesia ball is mainly used as a slag component conditioning agent for converter slag splashing protection furnace. Since the slag splashing furnace requires the proper viscosity and refractoriness of the slag, a reasonable slag composition is the key to the slag splashing protection. The usual slag can not directly carry out the splashing furnace, and it is necessary to take a certain amount of magnesium oxide balls for conditioning, and replace the use of dolomite together, reduce the amount of slag, and increase the content of MgO in the slag.
Since MgO is a high melting point mineral, the melting point is 2800 ° C, the MgO content in the slag advances, the slag viscosity becomes larger, the refractoriness advances, the slag is more easily combined with the lining, an effective slag protective layer is formed on the lining, and then the lining is advanced. Life expectancy and reduced consumption.
Light burnt magnesium balls are resistant to bending, pressure, high strength, gas hardening and gelling. They are widely used in defense, medicine, chemical, paper, shipbuilding and other occupations. In the building materials industry, it can be used to make fetal plates, particle boards, thermal insulation columns, railings, artificial marble, asbestos tiles, ordinary tiles, wall panels, and laying ground. With the advancement of science and technology, the use of light burnt magnesium powder is more extensive, and it can be used for civil engineering goods, light and heavy machinery packaging boxes, packaging bottom beams, high-temperature refractory materials, and can also produce beautiful and generous gloss furniture, which can be done in the machinery industry. Cast the model.
The light burnt magnesium ball is made by using the usually light burnt magnesium powder and mixing the ball after mixing. It is mainly used for converter steelmaking, slag splashing protection, and can advance the furnace age. The preparation of light burnt magnesium ball is to take 80% light burnt magnesium powder into 20% water, put it into the mixing mill for rolling, mixing and mixing for 15~2Omin to form a mixture, and send the ball press machine to produce the product through the belt conveyor. And then pile up. After the light burnt magnesium ball is dried for 48 hours and formed into strength, it is ready for sale.
The light burnt magnesium ball is used as a slag component conditioning agent for the converter slag splashing protection furnace. Since the slag splashing furnace requires the proper viscosity and refractoriness of the slag, a reasonable slag composition is the key to the slag splashing protection. The usual slag can not directly carry out the splashing furnace, and it is necessary to take a certain amount of magnesium oxide balls for conditioning, and replace the use of dolomite together, reduce the amount of slag, and increase the content of MgO in the slag.